Novel NaI improved Ge–Ga–Te far-infrared chalcogenide glasses

Abstract : In this study, a novel Te-based glass system was investigated. Some properties of Ge–Ga–Te–NaI chalcogenide glasses such as physical, thermal and optical transmitting were discussed. XRD patterns show this glass system with best amorphous state can dissolve content of NaI as much as 35 at.%. The lowest cut-off wavelength of glass samples is 1645 nm which is the smallest wavelength among the reported Te-based glasses doping with halide. DSC curves indicate that all glass samples have good thermal stabilities (ΔT > 100 °C) and the highest ΔT value corresponding to (Ge15Ga10Te75)85(NaI)15 glass is 120 °C which is 8 °C greater than that of Ge–Ga–Te host glass. The infrared spectra manifest Ge–Ga–Te–NaI chalcogenide glass system has a wide infrared transmission window between 1.6 μm and 20 μm. Consequently, Ge–Ga–Te–NaI glasses can be a candidate material for far infrared optic imaging and bio-sensing applications
Document type :
Journal articles
Complete list of metadatas

Cited literature [24 references]  Display  Hide  Download

https://hal-univ-rennes1.archives-ouvertes.fr/hal-01188223
Contributor : Laurent Jonchère <>
Submitted on : Wednesday, September 16, 2015 - 4:21:00 PM
Last modification on : Friday, July 10, 2020 - 4:21:55 PM
Long-term archiving on: : Tuesday, December 29, 2015 - 7:35:54 AM

File

Novel NaI improved - Ge-Ga-Te-...
Files produced by the author(s)

Identifiers

Citation

Ci Cheng, Xunsi Wang, Tiefeng Xu, Lihong Sun, Qingde Zhu, et al.. Novel NaI improved Ge–Ga–Te far-infrared chalcogenide glasses. Infrared Physics and Technology, Elsevier, 2015, 72, pp.148-152. ⟨10.1016/j.infrared.2015.07.024⟩. ⟨hal-01188223⟩

Share

Metrics

Record views

790

Files downloads

286