Weak polyelectrolyte multilayers as tunable membranes for solvent resistant nanofiltration

Abstract : This manuscript encompasses the investigation into the solvent resistant nanofiltration (SRNF) performance of multilayer membranes prepared from weak polyelectrolytes. These weak polyelectrolytes are unique in that the charge density is not fixed and depends on the coating pH, adding an extra variable as tuning parameter for SRNF performance. The weak polyelectrolyte based multilayers (PEMs) were prepared on a hydrolyzed PAN support membrane from poly(allylamine hydrochloride) (PAH) as polycation and poly(acrylic acid) (PAA) as polyanion. Detailed investigations on the role of the pH of the coating solution on the performance of the prepared SRNF-membranes were carried out with organic dyes of different size (~300–1000 Da) and charge. Variation in pH of the coating solutions was found to lead to a large degree of control over the separation performance of the prepared SRNF-membranes for the different dyes. The solvent permeabilities and the dye retentions were measured and correlated to variations in the PEM membrane structures, with more dye adsorption being found for membranes with more free acid and amine groups. The membranes were also found to be stable for long term-filtrations in solvents such as isopropyl alcohol (IPA), acetonitrile (ACN), tetrahydrofuran (THF) and in the challenging polar aprotic solvent, N,N-dimethylformamide (DMF). Results of this study clearly demonstrate the potential of using pH as tuning parameter for weak PEMs to prepare SRNF-membranes optimized for specific applications
Document type :
Journal articles
Complete list of metadatas

Cited literature [50 references]  Display  Hide  Download

https://hal-univ-rennes1.archives-ouvertes.fr/hal-01338527
Contributor : Laurent Jonchère <>
Submitted on : Thursday, September 15, 2016 - 12:09:50 PM
Last modification on : Friday, July 10, 2020 - 4:23:56 PM
Long-term archiving on: : Friday, December 16, 2016 - 1:35:56 PM

File

Weak polyelectrolyte multilaye...
Files produced by the author(s)

Identifiers

Citation

Shazia Ilyas, Nithya Joseph, Anthony Szymczyk, Alexander Volodin, Kitty Nijmeijer, et al.. Weak polyelectrolyte multilayers as tunable membranes for solvent resistant nanofiltration. Journal of Membrane Science, Elsevier, 2016, 514, pp.322-331. ⟨10.1016/j.memsci.2016.04.073⟩. ⟨hal-01338527⟩

Share

Metrics

Record views

212

Files downloads

175