Microhardness and optical property of chalcogenide glasses and glass‐ceramics of the Sn–Sb–Se ternary system - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of the American Ceramic Society Année : 2019

Microhardness and optical property of chalcogenide glasses and glass‐ceramics of the Sn–Sb–Se ternary system

Résumé

The microhardness of chalcogenide glasses (ChGs) of the Sn–Sb–Se (SSS) ternary system was investigated, and the correlation of microhardness with the mean coordination number of the SSS ChGs was determined. To prepare infrared‐transparent SSS glass‐ceramics (GCs), two SSS ChGs (A, Sn6.23Sb14.11Se79.66; B, Sn9.8Sb17.22Se72.98; by molar composition) were selected and thermally treated at 433 and 448 K, respectively. The improved microhardness (with values that increased by 11.5% and 7.3% for SSS ChG A and B, respectively) of the resulting SSS GCs is attributed to the formation of Sb2Se3 nanocrystals.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Xue et al. - Microhardness and optical property of chalcogenide.pdf (729.55 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01952379 , version 1 (12-12-2018)

Identifiants

Citer

Xuning Xue, Feifei Chen, Changgui Lin, Ruiqiang Lin, Xiaoyu Zhang, et al.. Microhardness and optical property of chalcogenide glasses and glass‐ceramics of the Sn–Sb–Se ternary system. Journal of the American Ceramic Society, 2019, ⟨10.1111/jace.15980⟩. ⟨hal-01952379⟩
17 Consultations
164 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More